Solvent-Free Epoxy Self-Leveling Topping (2.0-4.0mm) for Concrete Floors
EPOFLOOR SL (IFT) is a solvent free self-leveling floor topping based on formulated epoxy resin, and curing agents and silica sand specially selected for their ability to be applied and cured in warm temperatures.
EPOFLOOR SL (IFT) is supplied as a pre-measured kit depending on customers' requirements. Our standard packaging is 4 Liter & 15 Liter Kit.
EPOFLOOR SL (IFT) contains resin (Component A), hardener (Component B) and Silica Sand (Component C):
Keep in tightly closed containers and in sheltered and dry place with a temperature between +5°C and +35°C. In these conditions, it maintains its characteristics unchanged for 12 months.
| Solid Content | 100% |
| Recommended DFT / coat | 2.0 – 4.0mm |
| Kit Size | 4 Liters |
| Theoretical Coverage | 1.0 – 2.0 m2 / 4 liter kit |
| Kit Size | 15 Liters |
| Theoretical Coverage | 3.75– 7.5 m2 / 15 liter kit |
| Pot Life at 18°C | 90 minutes |
| Pot Life at 30°C | 40 minutes |
| Thin Layer (3mm) Dry Time at 25°C | 5-6 hours |
| Mixing Ratio HARDENER : BASE : SAND (by weight) | 1.0: 4.834 : 4.231 |
| Mixed Density at 20°C | 1.8 kg/L |
| Max Recoat/Topcoat Time at 25°C | 24 hours |
| Application Maximum Relative Humidity | 75 % |
| Compressive Strength (ASTM C579) | > 80 N / mm2 |
| Bending Strength (ASTM C580) | > 20 N / mm2 |
| Tensile Strength (ASTM C307) | > 12 N / mm2 |
| Bond Strength to Concrete (ASTM D4541) | > 2.0 N / mm2 |
| Taber Abrasion (ASTM D4060 CS17 Wheels) | 60 mg loss/1000cycles |
| Water Absorption (ASTM D413 ) (maximum) | 0.001% |
| Porosity with no sealer NACE Sand TM-01-74 | 0 |
| Hardness Shore D | 85 |
Application Thickness
A thickness of 2-4mm per coat over a primer is recommended.
Items Needed
Method
Adjust the rake to the desired thickness.
Using a drill and a paddle at low speed, stir the resin (Component A) for 1 min. Slowly add the hardener (Component B) and increase mixing speed. Mix for 1-2 minutes, ensuring proper mixing between both components A & B.
Slowly add the sand (Component C) and increase mixing speed. Mix for 1-2 minutes till a homogeneous streak free product is obtained.
Pour the mix onto the floor immediately and spread using the rake. After about 5 minutes use the spike roll to remove all entrapped air.
Cleaning
Clean equipment with SOLVENTE 10. In case of spillage, use fine silica or cement to absorb the spill and dispose of according to local regulations.
The concrete must be at least 28 days old. The concrete must be free from loose matter, oil and dirt before starting surface preparation.
The best method to prepare the surface is dry grinding using a specialized planetary grinder. Before grinding, the surface must be free from any degreasing or cleaning chemicals which may have been used. At the end of grinding, the surface should be flat.
Surface irregularities and blow holes shall be repaired with EPOFINISH IF.
When the filler is hardened, grinding and leveling of the patched area is recommended to ensure a good finish.
Ensure dust is removed from the surface using an industrial vacuum.
For best finish and adhesion, treat the surface with PRIMER POXY (IF). In case the surface is very absorbent, apply a second coat of primer within the allowed recoating time
Study the MSDS of the product before use or storage.
EPOFLOOR SL (IFT) is not regulated per the “Directive 67/548/EEC EU Dangerous Materials List” so no special labeling is needed
The information in this Technical Data Sheet is based on Colmef Monneli’s experience. Colmef Monneli does not accept any liability arising from the use of its products as it has no direct or continuous control over where or how its products are applied. All Colmef Monneli’s Data Sheets are updates on regular basis. It is the user’s responsibility to obtain the latest version.
Solvent-Free Repair Mortar for Concrete Floors
Solvent-Free Epoxy Topcoat for Concrete Floors
Solvent-Free Trowable Epoxy Mortar (5.0 - 20mm) for Concrete Floor
Medium Duty Polyurethane Hybrid Flooring
Heavy Duty Polyurethane Hybrid Flooring System
RUBBERIZED BITUMEN EMULSION