High Build Solvent Free Coal Tar Epoxy Coating
EPOSSITAR 100 CR is a two component solvent free epoxy polyamine coating, modified with low temperature tar. It is specially formulated for high build applications. Once cured, it produces a tough, flexible, chemical and impact resistant film.
Formulated to be easily applied, as thick as 200 microns in one coat. It provides excellent resistance to aggressive chemicals, water, acids, and alkalis.
Packaging:
EPOSSITAR 100 CR is supplied in 40 kg and 400 kg Kit.
Consumption:
Approximately 5m²/ Liter at 200 microns.
Storage:
Store generally in dry covered place with a temperature between +5ºC - +35ºC and RH below 70%. The expected shelf life of the product is 12 months from production date.
|
|||||||||||||||||||||||||||||||||||||||||||||||||||
Surface preparation
All surfaces must be dry, smooth, clean, sound, uncontaminated, and free from dust or loose material. Concrete surfaces must be fully cured and laitance must be removed by any suitable method.
For old concrete, all contamination must be removed and a sound clean substrate should be exposed, mechanical means of preparation are preferred followed by the removal of dust and other loose debris using an industrial vacuum.
Cracks should be reinforced with fibre mesh and must then be treated with epoxy mortar. Contact Colmef Technical Department for recommended products.
Mixing
Prior to application, stir component A (resin), then add component B (hardener) to it and mix thoroughly with a low speed electric drill (200 – 300 rpm) fitted with a suitable paddle to obtain a homogenous mixture.
Application
After mixing the two components, product will be ready for brush or airless spray application 5-10% SOLVENTE 10 may be added for airless spray application. Use nozzles of 0.21” – 0.025”, and working pressure 140 –160 bar. For brush or roller add 5% volume of SOLVENTE 10 if needed.
EPOSSITAR 100 CR is generally applied as a two coats application with a wet thickness of 200-300 micron per coat.
The hardening time vary sensitively according to environmental conditions and the type of support.
Cleaning
Tools and equipment should be cleaned with SOLVENTE 10 immediately after use. Hardened material should be removed mechanically. Spillages should be absorbed with sand or sawdust and disposed of in accordance with local regulations.
Recommendations
Keep the product away from sources of ignition.
During application, wear appropriate protective clothing, goggles, gloves and respiratory equipment. Avoid contact with skin, eyes and inhalation of vapour. Ensure proper ventilation at working place.
In case of contact with skin, rinse with water and again wash thoroughly with soap and water. In case of contact with eyes, rinse with plenty of water and seek medical advice accordingly.
If ingested, obtain medical attention immediately. Do not induce vomiting.
The information in this Technical Data Sheet is based on Colmef Monneli’s experience. Colmef Monneli does not accept any liability arising from the use of its products as it has no direct or continuous control over where or how its products are applied. All Colmef Monneli’s Data Sheets are updates on regular basis. It is the user’s responsibility to obtain the latest version.
Epoxy Polysulphide Elastomeric Coating
High Chemical Resistant Epoxy Coating
Water Based Epoxy Coating for Non-Toxic Applications
High Build Solvent Free Coal Tar Epoxy Coating
Coal Tar Epoxy Coating
SBR Bonding Agent for Cement Mortar & Concrete (General Purpose)