Single Component Polyurethane Joint Sealant
ELASTOSEAL PU25 is a high performance, single component moisture curing polyurethane, elastomeric joint sealant. When cures it forms a flexible, weather proof joint sealant with superior adhesion to most substrates.
600 ml sausage, 20 sausages per box.
The table below includes the coverage consumption in linear meter for 600mL pack (not including wastage):
Keep the product stored in a dry and covered area with temperature not more than 25ºC. The product maintains its stability for 12 months if stored as recommended.
Grey, beige, white (other colors available upon request with
minimum quantity requirement)
|Density at 25°C||
|Skinning time at 25°C||
|Elongation (ASTM D412-06a)||
|Tensile strength (ASTM D412-06a)||
|Modulus of elasticity at 100% (ASTM D412-06a) Hardness (ASTM D2240)||
|Shore A hardness (ASTM D2240)||
|Water retention (Average Moisture Loss) (ASTM C156-03)||
|Joint movement capacity (MAF)||
-50C to +800C
|Cure time at 25⁰C and 50% RH||
2 – 3 mm / 24 hours
|Temperature of application||
+50C to 350C
All values are subject to 5-10 % tolerance
Proper surface preparation is essential to grant a good bonding between the sealant and the substrate. Joint edges must be clean, dry, free from oil, dust, grease or any other contaminants materials that might affect bonding. Joint sides should be cleaned with wire brush. Sand blasting is recommended in case of deep contamination.
Damaged concrete edges of joint should be repaired with COLMEF concrete repair products.
On sound, clean, well prepared totally dry joint surfaces, Primer is not required. In case that primer is needed, use SEALPRIME for porous surface and seal SEALPRIME NP for non-porous surfaces.
In order that joint sealant function correctly the sealant must bond only to the sides of the joint and not to the bottom. Place CORDOFLEX Polyurethane closed cell backers at the bottom of the joint to ensure intimate contact of sealant with joint sides and to control sealant depth during application. In case that fixing of backing rod is not possible due to depth limitation, use adhesive backed polyurethane tape (bond breaker tape) to prevent joint bottom adhesion.
To be able to keep the joint edges clean, use masking tape on the joint sides and remove immediately after the sealant application has finished.
Apply SEALPRIME 1K Polyurethane to both side of the porous joint faces prior to installation of backer rod or bond breaking tapes by brushing in a thin uniform coat. Avoid applying too much primer as it may act as bond breaker.
For the porous substrates such as steel or glass, use SEALPRIME NP for optimum adhesion. Allow the primer to be tack free prior to application of the sealant.
ELASTOSEAL PU25 is available in a ready to use self-contained sausage which can be loaded onto a barrel gun. Start extruding the sealant into the joint firmly by maintaining an even pressure on the trigger of the gun. On vertical joint, sealant extrusion shall start from the bottom of the joint and continue to the top. Once the sealant has been installed a suitable rounded tool can be used to achieve a smooth profile.
Do not use soapy water solution. Excess sealant and smears adjacent to the joints should be removed before sealant cures.
Clean tools immediately after application with water.
ELASTOSEAL PU25 does not contain any hazardous substances.
During application, wear appropriate protective clothing, goggles, gloves and respiratory equipment if necessary.
In case of contact with skin, rinse with water and again wash thoroughly with soap and water. In case of contact with eyes, rinse with plenty of water and seek medical advice accordingly.
The information in this Technical Data Sheet is based on Colmef Monneli’s experience. Colmef Monneli does not accept any liability arising from the use of its products as it has no direct or continuous control over where or how its products are applied. All Colmef Monneli’s Data Sheets are updates on regular basis. It is the user’s responsibility to obtain the latest version.