High Build Flexible Polyurethane Floor Coating
A high performance Polyurethane coating specifically developed for use as a high build flexible floor coating.
Formulated on a complex blend of high molecular weight polyols and urethane polymers, which produces a system with outstanding impact and chemical resistance coupled with a high degree of flexibility. This unique resin system is combined with a special blend of pigments enabling a select range of colors to be offered suitable for the long term protection of industrial floors operating in the most aggressive of environments.
Packaging:
EPOFLOOR P200 is available in 4 and 15 Liter kits.
Consumption:
4–5 m2 / Liter per coat according to the porosity of the surface.
Storage:
Keep in tightly closed containers and in sheltered and dry place with a temperature between +5°C and +35°C. Shelf life is 12 months from date of production if stored properly.
|
Surface preparation
The surface of the concrete to be prepared shall be sound, clean and uncontaminated.
This preparation shall be such as to leave a sound exposed concrete surface free from dust, loose particles and any deleterious matter. If the concrete surface is defective or has laitance, it must be cut back to a sound base. Excess laitance deposits are best removed by light mechanical scrabbling, grinding or grit/captive blasting followed by vacuum cleaning to remove dust debris.
Any blowholes, chipping or similar surface imperfections shall be repaired using EPOFINISH C, a solvent free epoxy resin repair mortar.
Expansion joints shall be repaired using EPOMORT S, a high strength solvent free epoxy mortar.
New concrete or cementitious surfaces should be allowed to cure and have moisture content not exceeding 5%. Old or existing floor should be refurbished mechanically to ensure clear sound substrate.
Priming
Highly porous concrete must be treated with PRIMER PU, a high performance Epoxy primer. PRIMER PU shall be used as a primer coat for polyurethane based car park deck systems.
The primer should be applied by brush or roller on to the cleaned surface area (particularly hidden surfaces) at a rate of 6-8 m²/L.
The primer should be left to achieve a tack-free condition for 8-12 hours before applying the top coat. A second coat of primer may be required if the substrate is excessively porous.
Mixing
EPOFLOOR P200 is supplied in two pre-weighed packs (Component A – Base and Component B – Hardener) which are ready for immediate in-situ use. Stir in both components before use. Transfer the entire contents of component B (Hardener) into the component A (Base) can and mix with low speed drill and paddle (200 – 300 rpm) for 2 – 3 minutes till obtaining a mix with uniform consistency. Scrape the sides and bottom of the can during mixing to ensure homogeneity.
Application
Apply EPOFLOOR P200 by roller, squeegee or airless spray to the primed tack free surface. For airless pump applications, the product can be diluted with maximum 10% of SOLVENTE 10.
EPOFLOOR P200 can be applied as a single intermediate coat, or as a multi-coat sandwich system incorporating aggregates QUARTZO NO. 2 between coats to give a slip resistant finish.
Each coat is applied at a rate of 4-6m2/Liter achieving a thickness of 200-250 microns/coat. The total dry film thickness of the coating shall be a minimum of 500 microns.
Chemical Resistance
EPOFLOOR P200 is resistant to acids and alkalis of medium concentrations, mineral oil products and solvents.
Cleaning
Tools and equipment should be cleaned with SOLVENTE 10 from Colmef immediately after use. Hardened material should be removed mechanically. Spillages should be absorbed with sand or sawdust and disposed of in accordance with local regulations.
Recommendations
During application, wear appropriate protective clothing, goggles, gloves and respiratory equipment if necessary. In case of contact with skin, rinse with water and again wash thoroughly with soap and water.
In case of contact with eyes, rinse with plenty of water and seek medical advice accordingly. If ingested, obtain medical attention immediately. Do not induce vomiting.
The information in this Technical Data Sheet is based on Colmef Monneli’s experience. Colmef Monneli does not accept any liability arising from the use of its products as it has no direct or continuous control over where or how its products are applied. All Colmef Monneli’s Data Sheets are updates on regular basis. It is the user’s responsibility to obtain the latest version.
Seamless, Flexible, Polyurethane Flooring System
Seamless, Polyurethane Traffic Deck Coating System
Protective, Polyurethane Based Traffic Deck Coating System
Waterproofing and Protective, Polyurethane Based Traffic Deck Coating System
Waterproofing and Protective, Polyurethane Based Traffic Deck Coating System
SULPHATE RESISTANT BLOCK & BRICK LAYING MORTAR
Fairing Coat Solvent Free Epoxy Mortar (3mm or...
High Performance Epoxy Mortar
Polyurethane Primer